Galvanized wire is the use of cold-drawn low-carbon steel wire after galvanizing process of production of metal monofilament, according to the different galvanized process is divided into hot-dip galvanized wire and galvanized wire (cold galvanized wire). The hot-plating process is that the steel wire is immersed in the molten zinc solution to realize the coating, and the production process is faster than the electroplating process, Galvanized Barbed Wire the zinc content is large and the corrosion resistance is good, but the coating is uneven and the color is dark; the plating process is through the wire In the electrolysis to achieve the coating, relative to the hot-dip process production slow, small amount of zinc and poor corrosion resistance, but the coating uniform, Galvanized Barbed Wire the appearance of light. Galvanized iron wire due to low cost and good corrosion resistance and other characteristics, widely used in construction, Galvanized Barbed Wire handicrafts, screen preparation, product packaging and other industrial civilian areas.

Galvanized wire processing technology is divided into hot-dip plating and plating (cold plating). Hot-plating process for the wire through the 430 to 460 degrees high temperature melting state of the galvanized pool to complete the zinc liquid in the steel wire surface coating, Galvanized Barbed Wire and then finished by the completion of the production line, including helicopter and ramp up two, And by controlling the speed control on the amount of zinc. Galvanized Barbed Wire Electroplating process is in the plating tank through the current unidirectional so that zinc gradually coated with the surface of the wire process, in order to ensure the quality of galvanized, Galvanized Barbed Wire usually before and after the addition of a washing process, mainly used to remove the surface of impurities before electrolysis and removal of electrolysis After the wire surface residual plating.

(1) galvanized steel wire: high-quality low-carbon steel wire, wire diameter 2.0MM-4.0MM, Galvanized Barbed Wire wire tensile strength of not less than 380MPa, the surface of the wire using hot-dip galvanized protection, galvanized protective layer thickness Requires production, the maximum amount of galvanized up to 300 g / m 2.

(2) zinc-5% aluminum-mixed rare earth alloy steel wire: (also known as high-Seoul) steel wire, which is a recent international emerging material, Galvanized Barbed Wire corrosion resistance is more than three times the traditional pure galvanized steel wire The diameter of up to 2.0MM-4.0MM, wire tensile strength of not less than 380MPa.

(3) galvanized steel wire plastic: high-quality low-carbon steel wire, in the surface of the steel layer of PVC or PE protective layer, and then woven into a variety of wire cage This layer of protective layer will greatly increase in high pollution environment Protection, Galvanized Barbed Wire and through the choice of different colors, so that it can and the surrounding environment.

(4) zinc-5% aluminum-mixed rare earth alloy wire plastic: zinc-5% aluminum-mixed rare earth alloy wire on the surface of a layer of PVC or PE protective layer, Galvanized Barbed Wire and then woven into a variety of wire cage this layer of protection The layers will greatly increase the protection in highly polluted environments and will be able to blend with the surroundings through the choice of different colors.

(± 5%) Height tolerance (± 5%) between the side plate, Galvanized Barbed Wire the end plate, the end plate and the bottom plate, and the partition is separated by every 1 meter. Into a separate unit.

Second, the wire cage with assembly, cover, side panels, Galvanized Barbed Wire end plates, floor, separate production assembled into a cage, the various parts of the spiral wire wrapped around the cage all the silk are used to strengthen the strength of wire mesh box.